High Temperature Alloy Powder for (the Porous) Filter

 

Product Characteristics

1.Particle size distribution is uniform and narrow, passing rate is more accurate.

2.Using effective way to successfully reduce the apparent density of high temperature alloy powder and make pressing no longer difficult.?

3.Low oxygen level.

4.Particle size can be customized at any range.

5.The specia water atomization method results in a more limited particle size distnbution and can be controlled well. Apparent density can be selected at will.

 

Chemical Compositions of some items

  Cr Ni Mo W Cu S P C 0*10-6 Si Mn Fe Co V
Monel400 / 63/69 / / 28/34 ≤0.02
≤0.02
≤0.02
1000-2000 ≤1 ≤1 ≤2.5 / /
HastelloyC-22 20/22 Bal 12.5/14.5 2.5/3.5 / ≤0.04 ≤0.04 ≤0.08 3000-5000 ≤1 ≤1 2/6 ≤2.5 ≤0.35
HastelloyC-276 14.5/16.5 Bal 15/17 3/4.5 / ≤0.04 ≤0.04 ≤0.03 3000-5000 ≤1 ≤1 4/7 ≤2.5 ≤0.35
Inconel 600 14/17 Bal / / ≤0.5 ≤0.02 ≤0.02 ≤0.03 3000-5000 ≤0.5 ≤1 6/10 / /
Inconel 625 20/23 Bal 8/10 / / ≤0.02 ≤0.02 ≤0.03 3000-5000 ≤0.5 ≤1 ≤5 / /

 

Product Specification

State:Solid powder   Application area :Sintered Metal filter

Product Name

316L Stainless Steel Powder

Product Model

150-250μm


1. Chemical Composition (WT%):

Standard

IEC62321 Edition 1.0:2008, GB/T223.86-2009

Test Item

Test Result

C

≤0.03

O

≤2000ppm

S

≤0.02

P

≤0.02

Si

≤1

Cr

16/18

Ni

12/15

Mn

≤0.3

Mo

2-3

Fe

BAL


2. Physicals:

Standard
ISO3923-1:1979 , ISO 3953:1993 ,ISO 9276-4:2001
Test Item
Test Result
Apparent Density
(g/cm3)
1.8-2.1
Tap Density
(g/cm3)
--
Flow Rate
(s/50g)
30-40
Particle Size Distribution
Sieving(μm)
+250μm%
5%
-250+150μm%
Bal
-150μm%
5%